Argo-braze™ 502 brazing paste is a specially formulated paste product intended for use in semi or fully automated brazing processes, or where the use of a paste offers other advantages. It combines Argo-braze™ 502, a filler metal particularly suitable for tungsten carbide and PCD, in powder form with a flux-binder system selected to match an individual application. The resulting product is a fully dispensable, custom-made brazing paste ideal for brazing tungsten carbide and PCD segments.
AMS/AWS A5.8
4788, BAg-24

Argo-braze™ 56 brazing paste was developed to provide a paste solution for brazing of stainless steel where potential problem from interfacial corrosion on stainless steel components exposed to wet conditions in service might otherwise occur.

Argo-braze™ 632 brazing paste was as formulated provide a paste solution for brazing of stainless steel where potential problem from interfacial corrosion on stainless steel components exposed to wet conditions in service might otherwise occur. AMS/AWS A5.8
4774, BAg-21

Argo-braze™ 72V Brazing Paste is a specially formulated paste product. The product consists of Argo-braze™ 72V, a silver-copper brazing filler metal and a binder system which is normally not flux containing so suitable for furnace brazing applications.


AMS/AWS A5.8
BAg-8

EN1044:1999
AG401

Johnson Matthey B Bronze™ paste is a specialised copper based brazing paste. It is mainly used as a furnace-brazing paste for use on mild steel components where joint gaps are variable or too wide to use a standard copper paste.

EN1044:1999
CU105

C Bronze™ brazing paste was developed for furnace-brazing and is used for brazing carbide tipped drills. It contains manganese and nickel both of which provide improved wetting and bonding on cemented tungsten carbides. For this type of application with an air-hardening type of steel, simultaneous heat treatment of the tool shank, at temperatures between 800-1040°C is possible.

Johnson Matthey Copper 99.9% is a standard copper-based brazing paste. It was developed as a furnace-brazing paste and is a economic solution for brazing mild steel components with joints that provide an interference fit.
AMS/AWS A5.8
BCu-1

EN1044:1999
CU101

Silver-flo™ 55 Paint consists of a silver brazing filler metal powder (Silver-flo™ 55) and a brazing flux (Easy-flo™ Flux Powder) combined in a volatile organic solvent. The proportions of filler metal to flux are optimised to make the paint suitable for brazing small components by most heating methods.

The silver brazing filler metal in this product - Silver-flo™ 55, is cadmium-free. It combines a low brazing temperature with a short melting range, is very free flowing and produces neat joints with small fillets. These characteristics make it an excellent general purpose silver brazing filler metal.

Joints made with Silver-flo™ 55 Paint are suitable for seawater applications, being resistant to dezincification. The optimum joint gap for this filler metal at brazing temperature is normally 0.05-0.15mm.